PENGARUH REFINING PULP AMPAS TEBU (BAGASSE) TERHADAP STRENGTH PROPERTIES KERTAS TISSUE

Samudra, Bintar (2018) PENGARUH REFINING PULP AMPAS TEBU (BAGASSE) TERHADAP STRENGTH PROPERTIES KERTAS TISSUE. D4 thesis, Institut Teknologi Sains Bandung.

[thumbnail of TA_BINTAR SAMUDRA_124.14.021_AWAL.pdf] Text
TA_BINTAR SAMUDRA_124.14.021_AWAL.pdf

Download (883kB)
[thumbnail of TA_BINTAR SAMUDRA_124.14.021_BAB 1.pdf] Text
TA_BINTAR SAMUDRA_124.14.021_BAB 1.pdf

Download (107kB)

Abstract

Penelitian ini bertujuan untuk mengetahui fenomena beating pulp bagasse, mengetahui pengaruh csf terhadap sifat fisik ketas tissue dan mengetahui perbandingan sifat fisik kertas tissue dari pulp bagasse dan LBKP. Dengan menganalis nilai dari hasil uji softness, absorbency, tensile dan wet tensile. Sampel penelitian ini terdiri dari 30 lembar handsheet yang terbuat dari pulp bagasse dan 30 lembar handsheet yang terbuat dari LBKP sebagai pembanding. Handsheet didapatkan dengan melakukan pemasakan kraft pulping dari bagasse, yang kemudian dilanjutkan ke proses bleaching. Dengan jumlah total handsheet yang diuji sebanyak 60 lembar setelah dilakukan pengujian dengan hasil yang telah dianalisis diketahui bahwa hipotesis dapat diterima. Penelitian ini menyimpulkan bahwa nilai softness, tensile dan wet tensile dari pulp bagasse lebih tinggi dari LBKP denganselisih nilai softness sebesar 0.00271 mNm, tensile sebesar 0.003264 Nm/g dan wet tensile sebesar 0.003638 Nm/g. Sedangkan nilai absorbency yang diperoleh pulp bagasse lebih rendah dari LBKP dengan selisih nilai sebesar 20.8 mm.rnrnThis study aims to determine the beating of bagasse pulp, knowing the effect of physical conditions and knowing the physical condition of tissue paper from bagasse and LBKP. By analyzing the value of the test results of softness, absorbency, tensile and wet tensile. The research sample consisted of 30 handsheets made of pulp bagasse and 30 sheets of handsheets made from LBKP as a comparison. The handsheet is obtained by inserting kraft pulping from bagasse, which is then proceed to the bleaching process. With the total number of handsheets determined as many as 60 sheets after testing with successful results gained. This study concluded that the value of softness, tensile and wet tensile of pulp bagasse is higher than LBKP with a value of flexibility of 0.00271 mNm, tensile of 0.003264 Nm / g and wet tensile of 0.003638 Nm / g. While the absorption value obtained by the pulp pulp is lower than LBKP with a difference in value of 20.8 mm.

Item Type: Thesis (D4)
Contributors:
Contribution
Contributors/Pembimbing
NIDN
Thesis advisor
Susantini, Ni Njoman Manik
NIDN0408096804
Uncontrolled Keywords: Bagasse, Kraft pulping, Refining, Tissue
Subjects: Q Science > Q Science (General)
Divisions: Fakultas Vokasi > Teknologi Pengolahan Pulp dan Kertas
Depositing User: Perpustakaan ITSB
Date Deposited: 12 Jul 2024 03:16
Last Modified: 12 Jul 2024 03:16
URI: https://repository.itsb.ac.id/id/eprint/129

Actions (login required)

View Item
View Item